Abstract
The microstructures and mechanical properties of Mg–2.0Zn–1.0Mn (ZM21) alloys with certain amount of Ce and Nd additions were investigated, and the influence mechanism of Ce and Nd on the microstructures and mechanical properties of extruded alloys was discussed. The results indicated that the addition of Nd and Ce can refine the grains in ZM21 alloy, for which the distribution density of second phase particle played a major role to hinder the growth of dynamic recrystallization (DRX) grain in alloys by adding a content of 0.4 wt.% Ce and Nd. The average grain size of ZM21 alloy with the additions of 0.4 wt.% Nd and Ce reached 6 ± 3 μm and 13 ± 2 μm, respectively. Adding Ce and Nd to ZM21 alloy, the changes of mechanical properties were mainly attributed to a reduction in basal texture intensity, refinement grain size as well as the dispersion density and distribution position of fine second phase particles. Furthermore, by addition of Ce and Nd to ZM21 alloy, the non-basal plane slip system could be activated which decreased the basal texture intensity
چکیده
در این تحقیق، ریزساختار و خواص مکانیکی آلیاژهای( Mg-2.0Zn-1.0Mn (ZM21 با مقدار خاصی از Ce و Nd مورد بررسی قرار گرفته و مکانیزم تاثیر Ce و Nd بر ریزساختار و خواص مکانیکی آلیاژهای اکسترود شده مورد بحث قرار میگیرد. نتایج حاصله نشان می‌دهد که افزودن این دو عنصر می‌تواند منجر به اصلاح دانه‌ها درآلیاژ ZM21 شود و دانسیته توزیع ذره فاز ثانویه نقش مهمی در ممانعت از رشد دانه تبلور مجدد دینامیک (DRX) در آلیاژها با افزودن مقدار 0.4wt.% عناصر Ce و Nd دارد. اندازه دانه متوسط آلیاژ ZM21 با افزودن 0.4wt.% عناصر Ce و Nd به ترتیب به 6±3μm و 13±2μm رسید. با افزودن Ce و Nd به آلیاژ ZM21، تغییرات خواص مکانیکی عمدتا به کاهش شدت بافت قاعده، اصلاح اندازه دانه، دانسیته پراکندگی و موقعیت توزیع ذرات ریز فاز ثانویه ارتباط داده می‌شود. علاوه براین با افزودن Ce و Nd به آلیاژ ZM21، سیستم لغزش صفحه‌ای غیر قاعده می تواند فعال شود که شدت بافت قاعده‌ای را کاهش می دهد.