Abstract
Ultra-fine grain (UFG) Cu–Cr alloy is prepared by equal-channel angular pressing (ECAP). The microstructure, tensile and fatigue properties of the UFG Cu–Cr alloy were investigated. The bulk materials with average grain size of ∼230 nm were obtained through ECAP for 12 times. The cellular subgrains with low-angle grain boundaries were first formed at relatively low strains, and high-angle grain boundaries dominate the microstructure with the increasing of strains. Materials exhibit homogeneous equiaxed subgrains after ECAP processing. The Cu–Cr alloy processed by ECAP has high strength besides high conductivity and sufficient ductility. Fatigue experiments were carried out in terms of stress-controlled for the 4 and 6 passes ECAPed samples. The increase of fatigue limit and prolong of fatigue life are remarkable as compared with those of coarse grain Cu–0.75Cr alloy and ECAPed pure Cu reported in available literatures
چکیده
آلیاژ فوق ریزدانه(UFG)کرم- مس توسط روش پرس زاویه ای هم محور(ECAP) تهیه شد. ریزساختار، خواص خستگی وکششی آلیاژ فوق ریزدانه Cu-Cr مورد بررسی قرار گرفت. موادی با اندازه دانه nm230 توسط روش ECAP در طی 12 پاس به دست آمد. ریزدانه های سلولی با زاویه مرزدانه کم، درکرنش های اعمالی پایین تشکیل شده و با افزایش کرنش این زاویه افزایش یافت. مواد، ریزدانه های هم محور یکنواختی پس از فرآیند ECAP از خود نشان دادند.آلیاژ مس- کروم تشکیل شده توسط این فرآیند دارای استحکام بالا در کنار هدایت بالا و انعطاف پذیری مناسب می باشند. آزمون های خستگی برای قطعات 4 و 6 پاس پرس شده با روش تنش-کنترلی انجام گرفتند.آلیاژ تولید شده توسط روش ECAP حد خستگی و عمر خستگی بالاتری نسبت به آلیاژ درشت دانه Cu-0.75Cr و مس پرس شده نشان دادند.
1- مقدمه
مواد فوق ریز دانه تولید شده به روش ECAP در دهه ی اخیر به خاطر خواص فیزیکی و مکانیکی مناسب که عاری از تخلخل و ناخالصی هستند، مورد توجه بسیاری از محققان قرار گرفته اند. روش ECAP یک فرآیند کار سرد است که که کرنش های بسیار بالایی به حجم ماده بدون شکستن آن، برای ریزدانه کردن ماده، اعمال می کند...