The diffusion controlled corrosion of pipeline in the entrance region where the flow is developing was studied using the chemical dissolution of copper tubes in acidified FeCl₃ solution. Variables studied were solution velocity and pipe length. In addition, the effect of polyox drag reducing polymer on the rate of corrosion under turbulent flow conditions was tested. Dimensionless correlations were reached which can used to predict the rate of diffusion controlled corrosion under developing flow conditions which prevail in industrial equipment such as tubular reactors and heat exchangers. Drag reducing polymers were found to decrease the rate of corrosion by an amount ranging from 5 to 27% depending on polymer concentration and Reynolds number. Industrial implications of the present results were highlighted

چکیده 

انتشار كنترل شده خوردگی لوله در منطقه ورودی که در آن جریان در حال توسعه ميباشد، با استفاده از انحلال شیمیایی لوله­ های مس در محلول اسيدي كلريد آهن 3 (Fecl3) مورد بررسی قرار گرفته است. متغیرهای مورد مطالعه عبارتند از، سرعت محلول و طول لوله. علاوه بر این، اثر کاهش کشیدن پلیمر بر نرخ خوردگی تحت شرایط جریان آشفته مورد آزمایش قرار گرفته است. ارتباطات بدون بعد در اين ميان مطرح گشته که می­توانند جهت پیش­بینی نرخ انتشار كنترل شده خوردگی تحت شرایط جریان در حال توسعه که در تجهیزات صنعتی از جمله راکتورهای لوله و مبدلهای حرارتی غالب است، مورد استفاده قرار گيرند. مشخص شده است كه کاهش کشیدن پلیمر جهت کاهش میزان خوردگی به مقدار 5 تا 27 درصد به غلظت پلیمر و عدد رینولدز بستگي دارد. پیامدهای صنعتی حاصل از نتایج حاضر مورد توجه قرار گرفته است.

در عمل، لوله­ ها اغلب در جریان آشفته برای ملاحظات اقتصادی مورد عمليات قرار ميگيرند. در چنین شرایطی که در آن تنش برشی بالا است، فیلم هاي اکسید که ممکن است در دیواره داخلی خط لوله وجود داشته باشند، ممکن است با افزایش نرخ خوردگی منجر به افزایش نرخ انتقال جرم مربوط به اکسیژن محلول و / یا محصولات خوردگی بین محلول و دیوار لوله، گردند...