The synergistic stabilization effect of different metal lanolin fatty acids as natural-based thermal stabilizers for poly(vinyl chloride) (PVC) including calcium lanolin fatty acid (Calan2), zinc lanolin fatty acid (Znlan2) and lanthanum lanolin fatty acid (Lalan3) were studied through Congo red testing, color measurements, FTIR analyses and thermal behavior in this paper. The results showed that Lalan3/Calan2/Znlan2 stabilizers exhibited more excellent thermal stabilization efficiency to PVC than Calan2/Znlan2 thermal stabilizers, and the optimal mass ratio of Lalan3/Calan2/Znlan2 was 8:9:3. At last, the effect of degradation mechanism on PVC and synergistic stabilization was also investigated by FTIR analyses and thermal behavior
چکیده
اثر هم افزایی پایدار کنندگی اسیدهای چرب لانولین فلزی مختلف به عنوان استابلایزر حرارتی با پایه طبیعی برای پلی وینیل کلراید ازجمله اسید چرب لانولین کلسیم(Calan2)،اسید چرب لانولین روی(Znlan2) و اسید چرب لانولین لانتانیوم(Lalan3)از طریق تست Congo red،اندازه گیری رنگ،آنالیزهای FTIR، و رفتار حرارتی در این مقاله مورد مطالعه قرار گرفت .نتایج نشان داد که استابلایزرهای Znlan2/ Calan2/ Lalan3 پایدارکنندگی حرارتی بسیار عالی با بازدهی بیشتر برای PVC نسبت به استابلایزرهای حرارتی Znlan2/ Calan2 نشان می دهد.نسبت جرم بهینه برای Znlan2/ Calan2/ Lalan3 برابر با 8:9:3 بود .در پایان اثر مکانیسم تخریب PVC و هم افزایی پایدارکنندگی توسط رفتار حرارتی و آنالیز FTIR مورد بررسی قرار گرفت.
1-مقدمه
پلی وینیل کلراید که به اختصار PVC خوانده می شود سومین پلیمر ترموپلاستیک(گرما نرم) گسترده مورد استفاده بعد از پلی اتیلن و پلی پروپیلن است .وقتی که PVC به طور تصادفی در قرن 19 کشف شد مشخص شد که پایداری حرارتی پایین آن یک محدودیت اصلی برای کاربرد آن است. در مقایسه با سایر پلاستیک های مورد استفاده ،اشکال اصلی PVC پایداری حرارتی پایین در دمای پردازش است...